12% - 14% HADFIELD GRADE MANGANESE STEEL
APPLICATOR BARS AND PLATES
| FLATS |
ROUNDS |
SQUARES |
PLATES |
| SIZE |
SIZE |
SIZE |
SIZE |
SIZE |
SIZE |
DIAM |
THICKNESS |
THICKNESS |
| 3/16" x 2-1/2" |
3/8" x 1" |
1/2" x 1" |
3/4" x 1-1/2" |
1" x 1-1/2" |
1-1/2" x 2" |
5/16", 3/8" |
3/8" |
3/16", 1/4" |
| 1/4" X 1" |
3/8" x 1-1/2" |
1/2" x 1-1/2" |
3/4" x 2" |
1" x 2" |
1-1/2" x 6" |
1/2", 5/8" |
1/2" |
5/16", 3/8" |
| 1/4" x 1-1/2" |
3/8" x 2" |
1/2" x 2" |
3/4" x 2-1/2" |
1" x 2-1/2" |
|
3/4", 7/8" |
3/4" |
1/2", 3/4" |
| 1/4" x 2" |
3/8" x 3" |
1/2" x 2-1/2" |
3/4" x 3" |
1" x 3" |
|
1", 1-1/8" |
1" |
7/8", 1" |
| 1/4" x 3" |
3/8" x 4" |
1/2" x 3" |
3/4" x 4" |
1" x 4" |
|
1-1/4", 1-1/2" |
1-1/4" |
1-1/8", 1-1/4" |
| 1/4" x 4" |
3/8" x 4-1/2" |
1/2" x 3-1/2" |
3/4" x 5" |
1" x 6" |
|
1-3/4", 2" |
1-1/2" |
1-1/2", 1-3/4" |
| ANGLES |
3/8" x 5" |
1/2" x 4" |
3/4" x 6" |
1" x 8" |
|
2-1/4", 2-1/2" |
2" |
2", 2-1/4" |
| 2"x 2"x 1/4" |
3/8" x 6" |
1/2" x 5" |
|
|
|
3", 3-1/2" |
|
2-1/2", 3" |
|
|
|
1/2" x 6" |
|
|
|
4", 4-1/2" |
|
|
| |
|
|
|
|
|
5", 5-1/2" |
|
|
| |
|
|
|
|
|
6", 7" |
|
|
WEAR RESISTANT STEEL FOR HEAVY INDUSTRY
IT'S
USED HERE...FOR MAINTENANCE AND REPAIR:
QUARRY,
MINING, EXCAVATING AND COAL INDUSTRIES
- ROCK CRUSHER
JAWS, MANTLES & HAMMERS
- SHOVEL BUCKETS
- STONE CHUTES
- CONVEYOR CHAIN
WEARSTRIPS
- ELEVATOR BUCKETS
- QUARRY TRUCK
BOTTOMS
- CRUSHER LINERS
- BULLDOZERS AND
SCRAPERS
- MUCKERS
FOUNDRIES
& STEEL MILLS
- ORE BUCKETS
- SINTERING SEAL
BARS
- SHAKE-OUT MACHINES
- SHOT BLAST
CABINETS
- SCRAP HANDLING
EQUIPMENT
|
|
IT
DOES THIS...
- RESISTS SEVERE
IMPACT AND ABRASION
- WORK HARDENS
RAPIDLY UP TO 500/550 BRINELL
- RETAINS INNER
TOUGHNESS
- HAS VERY LOW
FRICTIONAL PROPERTY IN METAL-TO-METAL APPLICATIONS
- WELD WITH STULZ
MANGANESE-XL OR SIMILAR ELECTRODE
- CAN BE CUT BY
OXYACETYLENE TORCH
- HAS NON-MAGNETIC
PROPERTY FABRICATED PARTS TO SPECIFICATION
|
THIS IS WHAT IT IS ...
|
PHYSICAL PROPERTIES:
|
| Yield Strength |
60,000/85,000 psi |
| Tensile Strength |
120,000/130,000 psi |
| % Elongation in 2" |
35%/50% |
| Hardness as Rolled |
230/255 bhn |
| Work Hardens-up to |
550 bhn |
| Non-magnetic |
|
|
CHEMICAL ANALYSIS:
|
| Mn-12.0/14.0 |
Si.0.60 Max. |
| C-1.00/1.25 |
P-0.05 Max. |
| |
S-0.04 Max. |
WELDED, PUNCHED, DRILLED AND
FORMED FABRICATIONS WILL BE QUOTED
ON SUBMISSION OF SKETCH OR BLUEPRINT SPECIFICATIONS
|
|